Continuous use of functional refractories

refractory material
refractory material
With the development of continuous casting, the proportion of high-clean steel production increased, the sliding nozzle with a skateboard, long nozzle, the water inlet, the inlet, immersion nozzle and other flow control and blowing function of the need for a sharp increase in refractory materials. In contrast to the earlier use of imported bricks, such as the use of imported bricks, continuous casting refractory material are still dominated by domestic production of products.
Sliding with a skateboard, mainly the use of aluminum carbon, and later, due to improved materials, the use of improved conditions, greatly improved the number of durable. Material, due to the addition of zirconia, peeling resistance greatly improved. According to the experimental and stress calculation, the shape of the skateboard is improved, which suppresses the generation and expansion of the crack. Due to the miniaturization of the skateboard and the re-use of the rear skateboard, the consumption of the refractory brick is reduced, so that the iron making is propelled. On the other hand, the development of high-corrosive steel slabs such as Ca-treated steel and high-carbon steels has been developed. For example, an aluminum-magnesium carbon alkaline skateboard having both corrosion resistance and peeling resistance has been developed.
Long water nozzle is the most recent 10 years to improve the maximum refractory products, recently, long water mouth life can reach 30 furnace or 40 furnace is not surprising. Preheating, insulation and residue cleaning and other aspects of the use of improvements, for the extension of life has a significant effect. Material, the measures taken to strengthen the strength of the bowl material, to suppress the wear of the inner tube, to prevent external oxidation and to prevent peeling.
Submerged entry nozzle, its characteristics and the flow pattern within the mold and the relationship between the quality of slab larger, it is generally from the material and shape of the two aspects of development and improvement. Material development is representative of the nozzle inside the alumina difficult to attach the development of materials. Generally use ZrO2-CaO-C material, the recent widespread use of carbon-free lining. Shape of the development, there are ladder-type immersion nozzle, this nozzle can effectively prevent the bias current, reduce the nozzle inside the alumina adhesion. In addition, a scheme for the use of a swirling flow nozzle and a vortex flow nozzle with spherical protrusions is proposed, and a furnace test is underway.

More refractory material:
http://www.yilongrefractory.com/AllProductServlet?id=1&number=20
E-mail:sales8@chinaelong.com

没有评论:

发表评论